Our leader magnesia board wall is produced in zhangjiagang city China, which is widely known as MGO board producing base in whole world.
For magnesia board wall products, we have rich experience in researching and developing, producing, processing and trading. 10years in China.
This kind of goods uses proprietary processes with MGO, MgCl2, Perlite, fiberglass chip compounds to deliver multipurpose, versatile, non-combustible and unique material. This integral, hard, inert and paperless construction panel has good characteristics over panels made from gypsum, clay/wood and paper particles
Thickness: 3mm-20mm
Max length: 3000mm
Max width: 1220mm
Other sizes also be produced by costomers'need
Colors: White, red, green, grey and pink
Features:
1. Mineral based: The main ingredient is magnesium oxide environmentally friendly. It does not contain asbestos or any other known toxic material
2. Fireproof: A same material is used in some parts of the world to line industrial blast furnaces
3. Water resistant: And does not leach
4. Flexible: Does not break or crack easily. Wastage is therefore reduced. Flexibility is enhanced when wet.
5. Impact resistant: 6mm MGO boards are at the same level with 9-12mm gypsum boards. Thicker MGO boards 8-12mm are much stronger
Heading |
Unit Used |
Inspection value |
Standard |
Density |
kg/m³ . |
0.96-1.12g/cm³ |
GB/T7019-1997 |
Fire ratings |
grade |
A1 |
GB 8624 |
Thermal Resistance |
m² K/W |
1.14m² K/w |
GB/T13475-92 |
Bending Resistance (Dry) |
≤ Mpa |
18Mpa |
GB/T7019-1997 |
Bending Resistance (Fully Absorbed in Water) |
≤ Mpa |
22Mpa |
GB/T7019-1997 |
Sound Insulation |
dB |
≥ 44dB |
GBJ121-88 |
Absorption Moisture |
≤ % |
≤ 15% |
GB/T7019-1997 |
Tensile Strength |
≤ Mpa |
8-13Mpa |
GB/T7019-1997 |
Impact Resistance |
kj/m² |
Between 2.0-2.5 are qualified,
for 4mm, our board could reach 4.5 kj/m2.
so our boards are good. |
CNS 13778 |
Thickness |
mm |
3mm-20mm |
|
Specification |
mm |
1220*2440; 1200*2700; 1200*3000 |
|
Color |
|
white, grey, green and red |
|